  1. 4130 and 4140 comparison - Metal and Metallurgy ...

    May 26, 2010 · As the other posters have implied, the only reason to use 4130 instead of 4140 is if there is fusion welding required. If no welding is required and your tie rod is more than about 1/2 inch in diameter, use 4140. There's no real cost difference, and 4140 will give at least 30 percent higher tensile properties in a normalized condition, while 4130 vs 4140 steel4130 is better for welding but, for heat treating 4140 is even better because you can heat treat heavier sections for through hardness compared to4130 vs 4140 steelSteering tie rods made from 4140 can be suitable for your proposed end use. You must process them in the appropriate manner - raw material, formin4130 vs 4140 steelWhat heat treatment are you specifying? What is the industry precident or standard? My seat of the pants feeling is that either alloy would suffic4130 vs 4140 steelsteve37, As the other posters have implied, the only reason to use 4130 instead of 4140 is if there is fusion welding required. If no welding is r4130 vs 4140 steel1Thanks for the help guys. The O.D. of the tie rods will be .875". When I thread on the lathe, I usually cut in a relief at the end for the end of t4130 vs 4140 steelWe had this issue once for wheelchair axle components. 4130 is specified in a lot of aircraft applications, so many people assume it is "better" m4130 vs 4140 steelHow do tie rods fail in this service? - Direct bending from side loads ( drive over large rock and tie rod is asked to support weight of vehicle fo4130 vs 4140 steelSteve, Please don't take this as a personal attack; but - Lesson for everyone, the OP's customer wanted a specific material, the OP recommended ano4130 vs 4140 steelYou are right! I began "roughing out" the material then stopped, thought about it and figured I better get some answers before I go any further. Th4130 vs 4140 steelTmoose, Usually the problem is hitting a boulder. They are covered with Nevada silt and hard to spot. Also, they like to hide behind a bush. Brakin4130 vs 4140 steelSee more results

  2. Steel Comparison: 4130 VS 4340 Steel - Otai Special Steel

    We supply a lots of 4130 and 4340 steel grades to our customers all over the world. You will find the chemical and mechanical properties comparison between steel 4130 vs 4340 steel grades as below. And it may help for machining purposes and as a reference for your purchasing 4130 steel and 4340 steel. 4130

  3. Differences Between Normalized and Annealed 4130 Steel ...

    See more on hunker.com

  4. Differences between 4130 and 4140 steels? [Archive] - The ...

    If I understand things correctly, the chemical difference between 4130 and 4140 steels are 0.1% more carbon in the 4140. That right? How about machinability? I have 2 very small projects that suggest hex 4130. I haven't found hex in 4130 but 4140. Close enough? Will

  5. Using 4140 alloy on your suspension parts verses 4130 ...

    Jan 11, 2013 · This means that technically 4130 lives smack dab equally distant between 1020 mild steel and 4140. This demonstrates how much of a difference "only .1% makes in the steel world. 4140 also has a really high manganese content (An element used to control sulfur) which means that the chances of delaminations in the steel are greatly increased.

  6. 4130 vs 4140 - practicalmachinist.com

    Sep 21, 2006 · is this 4140 pre hardened or annealed? The 4130 I am familiar with is AQ annealed and it works about twice as easy as 4140 pre hardened. 4140 annealed should be very similar and hardly noticeable above 4130, IMHO, but it depends on sizes and what you are doing with it. carbide won't notice a difference, drilling will.See more results

  7. How do I Compare 4140 & 4150 Steel?, Sciencing

    Mixing steel with various amounts of other elements produces steel alloys with mechanical properties superior to steel alone. SAE 4140 and 4150 steels are standard alloy steels. The major criteria used for comparing alloy steels are chemical composition and tensile strength.

  8. AISI 4130 Alloy Steel (UNS G41300) - AZoM.com

    Tempering of AISI 4130 steel can be performed at 399 to 566°C (750 to 1050°F), depending on the desired strength level. Hardening of AISI 4130 steel can be done with cold working or heat treatment. Some of the major applications of AISI 4130 alloy steel are in aircraft engine mounts and welded tubing.

  9. AISI 4130 Steel, 25CrMo4, 1.7218, 708A25, SCM430 ...

    What is 4130 steel?. AISI 4130 alloy steel is a medium carbon, low alloy steel in ASTM A29 standard. ASTM 4140 steel is also commonly referred to as a chromoly steel, or chrome moly steel, containing nominally 0.28-0.33% Carbon, 0.8-1.1% Chromium and 0.15-0.25% Molybdenum.Some results are removed in response to a notice of local law requirement. For more information, please see here.

  10. Differences between 4130 and 4140 steels? [Archive] - The ...

    If I understand things correctly, the chemical difference between 4130 and 4140 steels are 0.1% more carbon in the 4140. That right? How about machinability? I have 2 very small projects that suggest hex 4130. I haven't found hex in 4130 but 4140. Close enough? Will

  11. How do I Compare 4140 & 4150 Steel?, Sciencing

    Mixing steel with various amounts of other elements produces steel alloys with mechanical properties superior to steel alone. SAE 4140 and 4150 steels are standard alloy steels. The major criteria used for comparing alloy steels are chemical composition and tensile strength.

  12. AISI 4130 Steel, 25CrMo4, 1.7218, 708A25, SCM430 ...

    What is 4130 steel?. AISI 4130 alloy steel is a medium carbon, low alloy steel in ASTM A29 standard. ASTM 4140 steel is also commonly referred to as a chromoly steel, or chrome moly steel, containing nominally 0.28-0.33% Carbon, 0.8-1.1% Chromium and 0.15-0.25% Molybdenum.

  13. Using 4140 alloy on your suspension parts verses 4130 ...

    Jan 11, 2013 · This means that technically 4130 lives smack dab equally distant between 1020 mild steel and 4140. This demonstrates how much of a difference "only .1% makes in the steel world. 4140 also has a really high manganese content (An element used to control sulfur) which means that the chances of delaminations in the steel are greatly increased.

  14. AISI 4130 Alloy Steel (UNS G41300) - AZoM.com

    Tempering of AISI 4130 steel can be performed at 399 to 566°C (750 to 1050°F), depending on the desired strength level. Hardening of AISI 4130 steel can be done with cold working or heat treatment. Some of the major applications of AISI 4130 alloy steel are in aircraft engine mounts and welded tubing.

  15. AISI 316 Stainless Steel vs. Annealed SAE-AISI 4130 ...

    Both AISI 316 stainless steel and annealed SAE-AISI 4130 are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

  16. AISI 4130 vs AISI 8620 - Metal and Metallurgy engineering ...

    Dec 27, 2011 · AISI 4130 vs AISI 8620 gafoorkti (Materials) (OP) 18 Dec 11 11:03. 4130 vs 4140 steel We use 8630 and 4130 interchangeabily for some parts as they both belong to low alloy carbon steel family and can be heat treated to the design strength level, if no welding involved. This is clearly a non-conformance from your PO or Spec, but it may be acceptable.

  17. 4140 ht verses 4142 ht - Material engineering general ...

    For AISI 4140 versus AISI 4142 the only main difference is the carbon content, and it's pretty small. The balance of the chemistry is the same. 4130 vs 4140 steel 4142 HT Turned, Ground and Polished is a chromium-molybdenun alloy steel that has been hardened to 27 to 32 Rockwell C and is ready to use while still machinable and of exceedingly high strength 4130 vs 4140 steel

  18. 41xx steel - Wikipedia

    41xx steel is a family of SAE steel grades, as specified by the Society of Automotive Engineers (SAE). Alloying elements include chromium and molybdenum, and as a result these materials are often informally referred to as chromoly steel (common variant stylings include chrome-moly, cro-moly, CrMo, CRMO, CR-MOLY, and similar).

  19. Shafts: 4140 vs 4150? - Metal and Metallurgy engineering ...

    Jan 30, 2004 · Shafts: 4140 vs 4150? sprintcar (Mechanical) 4130 vs 4140 steel For a shaft of 12 inch diameter I believe that you would be better served using a higher alloy steel such as 4340 or better. This steel has superior hardenability response during heat treatment compared to either 4140 or 4150, that is, it will give superior tensile&yield strengths and other 4130 vs 4140 steel

  20. AISI 4130 Alloy Steel - 4130 Steel Forgings, All Metals ...

    AISI or SAE 4130 grade is a low-alloy steel containing chromium and molybdenum as strengthening agents. The steel has good strength and toughness, weldability and machinability. Type 4130 steel should be forged between 2250 and 1750 º F (1230 and 950 º C.).

  21. Machining 4130 (prehard or Annealed?) - practicalmachinist.com

    Nov 30, 2011 · 4130 has a machinability rating of about 35%, meaning your speed will be about 1/3 that of mild steel. Using carbide try about 100 SFPM and HSS about 30 SFPM. 38Rc is not a problem with carbide, might have to run slower. 4130 hardens about 1" deep so if

  22. Use of Mild steel vs 4130 - Welcome to The Aerodrome

    Jul 11, 2008 · Use of Mild steel vs 4130 Reply. Quote: Originally Posted by wilhelm. I would like to know the pros and cons in using mild steel vs 4130 chromoly for control surfaces like rudders and elevators. Has anyone priced chromoly steel these days. Willie. Hello Willie,Some results are removed in response to a notice of local law requirement. For more information, please see here.

  23. Welding 4140 versus 4130 - weldingweb.com

    Dec 12, 2007 · btw, there isn't much difference in welding or other material properties from 4130 to 4140 steel. All the alloy change did was bump the carbon content from 0.30% to 0.40%. Changing from 4130 to 4340 is a bigger change, because you are not only changing the carbon content slightly but also changing from a cro-moly alloy to a cro-moly-nickel 4130 vs 4140 steel

  24. D2 steel|4130 steel|4140 steel|H13 steel|AISI 4340 steel ...

    Dongguan songshun mould steel CO.,LTD.as China's largest steel wholesalerMain Steel has4140 steel,D2 steel,4130 steel,H13 steel,P20 steel,AISI 4340 steel,1.2738 steel,1.2379 steel,1.2344 steel,1.2080 steelWelcome to your contactE-mail:songshun.mould.steel@gmail.com, TEL86-0769

  25. AISI 4130 Alloy Steel - 4130 Steel Forgings, All Metals ...

    AISI or SAE 4130 grade is a low-alloy steel containing chromium and molybdenum as strengthening agents. The steel has good strength and toughness, weldability and machinability. Type 4130 steel should be forged between 2250 and 1750 º F (1230 and 950 º C.).

  26. Use of Mild steel vs 4130 - Welcome to The Aerodrome

    Jul 11, 2008 · Use of Mild steel vs 4130 Reply. Quote: Originally Posted by wilhelm. I would like to know the pros and cons in using mild steel vs 4130 chromoly for control surfaces like rudders and elevators. Has anyone priced chromoly steel these days. Willie. Hello Willie,

  27. AISI 316 Stainless Steel vs. Annealed SAE-AISI 4130 ...

    Both AISI 316 stainless steel and annealed SAE-AISI 4130 are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

  28. AISI 4130 vs AISI 8620 - Metal and Metallurgy engineering ...

    Dec 27, 2011 · AISI 4130 vs AISI 8620 gafoorkti (Materials) (OP) 18 Dec 11 11:03. 4130 vs 4140 steel We use 8630 and 4130 interchangeabily for some parts as they both belong to low alloy carbon steel family and can be heat treated to the design strength level, if no welding involved. This is clearly a non-conformance from your PO or Spec, but it may be acceptable.

  29. Machining 4130 (prehard or Annealed?) - practicalmachinist.com

    Nov 30, 2011 · 4130 has a machinability rating of about 35%, meaning your speed will be about 1/3 that of mild steel. Using carbide try about 100 SFPM and HSS about 30 SFPM. 38Rc is not a problem with carbide, might have to run slower. 4130 hardens about 1" deep so if

  30. 4140 vs 4340 - Material engineering general discussion ...

    Jul 09, 2002 · 4140 vs 4340 4140 vs 4340 JamesBarlow (Mechanical) (OP) 9 Jul 02 11:16. I am currently having a discussion about the differences between 4140 and 4340. They seem pretty similar chemically and mechanically, based on the book information I have.

  31. What's EN19 steel, and similar to 4140 steel grade ...

    EN19 Steel is one steel grade in BS 970-1955 standard, which is specification for wrought steels for mechanical and allied engineering purpose. Although there is new version of BS 970-1996 latest edition. And EN19 steel grade is similar to 709M40 grade in new version. The EN19 steel equivalent grades are AISI 4140, DIN 1.7225/ 42crmo4. There 4130 vs 4140 steel

  32. AISI 4140 Alloy Steel (UNS G41400) - azom.com

    AISI 4140 alloy steel can be cold worked using conventional methods in the annealed condition. Annealing. AISI 4140 alloy steel is annealed at 872°C (1600°F) followed by slowly cooling in the furnace. Tempering. AISI 4140 alloy steel can be tempered at 205 to 649°C (400 to 1200°F) depending upon the desired hardness level.

  33. 4140 vs 4150, The High Road

    Feb 16, 2008 · 4140 is also a bit less expensive in bulk than 4150 and because of the properties, chrome will adhere to 4150 a bit better than 4140 I agree that 410 and 416 stainless steels are better barrel steels than 4140 or 4150 chrome moly, especially if they have been cyrogenically treated to relieve stresses.

  34. TECHNICAL: LRG 4140 vs 4130 Lanternmark

    4140 is similar in composition to 4130 except for the higher carbon content. The 30 in 4130 represents the carbon content by % of weight (0.28-0.33 % for 4130 vs 0.38-0.43 % for 4140). Because of its higher carbon content, 4140 steel has greater hardenability and strength than does 4130.

  35. Difference between 4140 and 4140H steel - CR4 Discussion ...

    May 12, 2010 · Difference between 4140 and 4140H steel 05/12/2010 1:18 PM Hi I am trying to understand difference betwen thees two alloys, constituent composition and percentages are

  36. 4140 ht verses 4142 ht - Material engineering general ...

    For AISI 4140 versus AISI 4142 the only main difference is the carbon content, and it's pretty small. The balance of the chemistry is the same. 4130 vs 4140 steel 4142 HT Turned, Ground and Polished is a chromium-molybdenun alloy steel that has been hardened to 27 to 32 Rockwell C and is ready to use while still machinable and of exceedingly high strength 4130 vs 4140 steel